MODELIT KRONOS fast casting polyurethane 10 kg + 8 kg

<h2>&nbsp;MODELIT KRONOS</h2>

<p>Used mainly in electronics, prototype making, souvenirs making, picture and mirror frames, climbing holds, furniture parts, machine castings...</p>

<p>&nbsp;</p>

<p>ADVANTAGES</p>

<p>●&nbsp;&nbsp; quick hardening</p>

<p>●&nbsp;&nbsp; low viscosity</p>

<p>●&nbsp;&nbsp; low shrinkage</p>

<p>●&nbsp;&nbsp; easy-to-use mixing ration(100:80&nbsp;by weight)</p>

<p>●&nbsp;&nbsp; High filler content possible while retaining a low viscosity</p>

<p>&nbsp;</p>

<p>APPLICATIONS</p>

<p>Prototypes and&nbsp;patterns by casting in silicone moulds, negatives, molds, masters,figurines and mock-ups using the unfilled product or filled with mineral, metallic fillers and pigments.</p>

<p>Colour with VIVAT pigments or pigment pastes.</p>

<p>&nbsp;</p>

<p>For molds, use MODRIN MF silicone rubber or epoxy resin EPOX 210. Apply a release agent if using an EPOX 210 mold.</p>

<p>&nbsp;</p>

<p>&nbsp;</p>

<p>Mixing ratio Comp. A : Comp. B&nbsp; &nbsp; &nbsp;100 : 80</p>

<p>Pot life (100 g at 20&deg;C): 90 to 110 seconds</p>

<p>Demoulding time:&nbsp; 4 - 6 minutes</p>

<p>&nbsp;</p>

<p>Colour (mixture): beige</p>

<p>Hardness: 73-75 Shore D (at 23&deg;C, ISO 868)</p>

<p>Elongation at break 6,4 %&nbsp; &nbsp;(ISO R 527)</p>

<p>Charpy impact resistance kJ/m&sup2; 37&nbsp; (ISO 179)</p>

<p>Viscosity (at 23&deg;C)</p>

<p>&nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; comp. A&nbsp; &nbsp; cPs&nbsp; 100</p>

<p>&nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; &nbsp; comp. B&nbsp; &nbsp;cPs&nbsp; 165</p>

<p>Fluxural modulus of elasticity mPa&nbsp; 1.750&nbsp; (ISO 178)</p>

<p>Shrinkage 1,5 %</p>