Used mainly in electronics, prototype making, souvenirs making, picture and mirror frames, climbing holds, furniture parts, machine castings...
● quick hardening
● low viscosity
● low shrinkage
● easy-to-use mixing ration(100:80 by weight)
● High filler content possible while retaining a low viscosity
Prototypes and patterns by casting in silicone moulds, negatives, molds, masters,figurines and mock-ups using the unfilled product or filled with mineral, metallic fillers and pigments.
Colour with VIVAT pigments or pigment pastes.
For molds, use MODRIN MF silicone rubber or epoxy resin EPOX 210. Apply a release agent if using an EPOX 210 mold.
Mixing ratio Comp. A : Comp. B 100 : 80
Pot life (100 g at 20°C): 90 to 110 seconds
Demoulding time: 4 - 6 minutes
Colour (mixture): beige
Hardness: 73-75 Shore D (at 23°C, ISO 868)
Elongation at break 6,4 % (ISO R 527)
Charpy impact resistance kJ/m² 37 (ISO 179)
Viscosity (at 23°C)
comp. A cPs 100
comp. B cPs 165
Fluxural modulus of elasticity mPa 1.750 (ISO 178)
Shrinkage 1,5 %